University of SaskatchewanHARVEST
  • Login
  • Submit Your Work
  • About
    • About HARVEST
    • Guidelines
    • Browse
      • All of HARVEST
      • Communities & Collections
      • By Issue Date
      • Authors
      • Titles
      • Subjects
      • This Collection
      • By Issue Date
      • Authors
      • Titles
      • Subjects
    • My Account
      • Login
      JavaScript is disabled for your browser. Some features of this site may not work without it.
      View Item 
      • HARVEST
      • Electronic Theses and Dissertations
      • Graduate Theses and Dissertations
      • View Item
      • HARVEST
      • Electronic Theses and Dissertations
      • Graduate Theses and Dissertations
      • View Item

      Hydrotreating of light gas oil using carbon nanotube supported NiMoS catalysts : influence of pore diameters

      Thumbnail
      View/Open
      StefanSigurdsonMastersThesis.pdf (8.577Mb)
      Date
      2009-12
      Author
      Sigurdson, Stefan Kasey
      Type
      Thesis
      Degree Level
      Masters
      Metadata
      Show full item record
      Abstract
      Multi-walled carbon nanotubes (MWCNTs) are a potential alternative to commonly used catalyst support structures in hydrotreating processes. Synthesis of MWCNTs with specific pore diameters can be achieved by chemical vapor deposition (CVD) of a carbon source onto an anodic aluminum oxide (AAO) template. AAO films consist of pore channels in a uniform hexagonal arrangement that run parallel to the surface of the film. These films are created by the passivation of an aluminum anode within an electrolysis cell consisting of certain weak acid electrolytes. Changing the concentration of the electrolyte (oxalic acid) and the electrical potential of the electrolysis cell altered the pore channel diameter of these AAO films. Controlling the pore diameter of these templates enabled the pore diameter of MWCNTs synthesized by CVD to be controlled as well. The produced MWCNTs were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), Raman spectroscopy, and N2 adsorption analysis. Anodizing conditions of 0.40 M oxalic acid concentration and 40.0 V maximum anodizing potential were found to produce AAO films that resulted in MWCNTs with optimum surface characteristics for a catalyst support application. CVD parameter values of 650°C reaction temperature and 8.00 mL/(min·g) C2H2-to-AAO ratio were found to produce the highest yield of MWCNT product. The MWCNTs were synthesized for the purpose of supporting hydroprocessing catalysts, with several grades of NiMo/MWCNT sulfide catalysts being prepared to determine the optimum pore size. These catalysts were characterized by techniques of TEM, CO chemisorption, N2 adsorption, and H2 temperature programmed reduction (TPR). A MWCNT grade with 67 nm inner diameters (found from TEM analysis) was found to offer the best hydrodesulfurization (HDS) and hydrodenitrogenation (HDN) activities for the treatment of coker light gas oil (CLGO). After determining the most suitable pore diameter, the optimum catalyst metal loadings were found to be 2.5 wt.% for Ni and 19.5 wt.% for Mo. The optimum catalyst was found to offer HDS conversions of 90.5%, 84.4%, and 73.5% with HDN conversions of 75.9%, 65.8%, and 55.3% for temperatures of 370°C, 350°C, and 330°C, respectively. An equal mass loading of commercial NiMo/ã-Al2O3 catalyst offered HDS conversions of 91.2%, 77.9%, and 58.5% with HDN conversions of 71.4%, 53.2%, and 31.3% for temperatures of 370°C, 350°C, and 330°C, respectively. A kinetic study was performed on the optimum NiMo/MWCNT catalyst to help predict its HDS and HDN activities while varying the parameters of temperature, liquid hourly space velocity (LHSV), pressure, and gas-to-oil flow rate ratio. Rate expressions were then developed to predict the behavior of both the HDS and HDN reactions. Power law models were best fit with reaction orders of 2.6 and 1.2, and activation energies of 161 kJ/mol and 82.3 kJ/mol, for the HDS and HDN reactions, respectively. Generalized Langmuir-Hinshelwood models were found to have reaction orders of 3.0 and 1.5, and activation energies of 155 kJ/mol and 42.3 kJ/mol, for the HDS and HDN reactions, respectively.
      Degree
      Master of Science (M.Sc.)
      Department
      Chemical Engineering
      Program
      Chemical Engineering
      Supervisor
      Dalai, Ajay; Adjaye, John
      Committee
      Nui, Catherine; Soltan, Jafar; Wilson, Lee
      Copyright Date
      December 2009
      URI
      http://hdl.handle.net/10388/etd-01072010-162623
      Subject
      reaction kinetics
      gas oil hydrotreating
      heterogeneous catalysis
      carbon nanotubes
      anodized alumina
      Collections
      • Graduate Theses and Dissertations
      University of Saskatchewan

      University Library

      © University of Saskatchewan
      Contact Us | Disclaimer | Privacy