Coatings for alloys used in molten salt nuclear reactor
Date
2022-02-23
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
ORCID
Type
Thesis
Degree Level
Doctoral
Abstract
Rising CO2 levels due to the production of energy from fossil fuels are major contributors to
environmental pollution. Nuclear energy, on the other hand, is clean energy and does not contribute
to environmental pollution. Conventional water-cooled reactors are safe; however, they still suffer
the consequences of the Fukushima accident. A molten salt-cooled reactor, on the other hand, is
intrinsically safe and more efficient. But the problem of corrosion of structural alloys in a molten
salt environment is an obstacle to the success of Molten Salt Reactors (MSR). The purpose of this
research is to analyze the corrosion behaviour of different alloys in a molten salts environment and
develop coatings for inhibiting this corrosion.
The alloys Hastelloy® N, Haynes® X-750, AISI 304, and AISI 316 were tested for corrosion in
molten FLiNaK for 100 h at 700 °C under an argon gas cover. The Cr depletion was found to be
the major cause of corrosion in the FLiNaK environment. The highest corrosion observed in the
Haynes® X-750, is related to the presence of Al and Ti. However, Hastelloy® N is well protected
against corrosion in the FLiNaK environment.
Furthermore, AISI 316 was coated with Ni of varying thicknesses to see its corrosion resistance
behaviour in FLiNaK at 700 °C. The results indicate thicker Ni coatings of 75 µm are sufficient to
provide corrosion resistance to the stainless-steel samples under the testing conditions. But the
chromium was still observed to be diffusing toward the Ni coating from the steel substrate and
could eventually lead to corrosion during longer exposures to FLiNaK salt. The Ni coating was
also modified with the addition of Mo to evaluate the corrosion resistance in the FLiNaK
environment. The AISI 304 samples coated with Ni-Mo did not protect well against corrosion. The
presence of Mo in the Ni-Mo coating was associated with the formation of carbides at the surface
of the Ni-Mo coated sample, which led to accelerated corrosion.
Finally, a SiC diffusion barrier was deposited between the Ni plating and the steel surface. The
results obtained showed that this coating improved the corrosion resistance of the AISI 304
samples by five times.
Description
Keywords
Molten Salt Corrosion, Molten Salt Reactor, Hastelloy N, FLiNaK